Thermal stability of plasma-sprayed La₂Ce₂O₇/YSZ composite coating

A composite coating composed of La₂Ce₂O₂ (LCO) and yttria-stabilized zirconia (YSZ) in a weight ratio of 1:1 was deposited by the plasma spraying using a blended YSZ and LCO powders, and the stability of the LCO/YSZ interface exposed to a high temperature was investigated. The LCO/YSZ deposits were exposed at 1300 °C for different durations. The microstructure evolution at the LCO/YSZ interface was investigated by quasi-in-situ scanning electron microscopy assisted by X-ray energy-dispersive spectrum analyses and X-ray diffraction measurements. At an exposure temperature of 1300 °C, the grain morphology of LCO splats in contact with YSZ splats changed from columnar grains to quasi-axial grains with interface healing, and some grains tended to disappear during the thermal exposure. The results indicate that the phases in LCO-YSZ composite coating are not stable at 1300 °C. The element La in the LCO splat diffused towards the adjacent YSZ splat during the exposure, generating the reaction product layers composed of La₂Zr₂O₇ between the LCO and YSZ splats. After exposed for 200 h, the composite coating consisted of a mixture of mainly La₂Zr₂O₇ and CeO₂ and a minor amount of YSZ, accounting for the unusual decrease in the thermal conductivity at the late stage of exposure.