Stability and thermodynamic properties of supersaturated solid solution and amorphous phase formed by ball milling in the Zr- Al system

Zr ₁₀₀-_xA1_x (x ≤ 40) metastable alloys were synthesized by high- energy ball milling of elemental Zr and Al powders: supersaturated substitutional cph solid solution for x ≤ 15 and an amorphous phase for x ≥ 17.5. We performed a calorimetric study of the thermodynamics and kinetics of the metastable- to- equilibrium transformations of these phases. Their stability range (temperature/composition), as well as the apparent activation energies associated with the transformations, were determined. The transformation enthalpies were measured and used to determine the enthalpy of formation for these metastable phases. For both as- milled and relaxed amorphous phases, the measured enthalpy of crystallization is compared with those estimated for an undercooled liquid. Different amounts of retained entropy at the glass transition temperature were used to estimate the enthalpy loss upon undercooling due to the excess specific heat.