Preparation and oxidation behavior of three-dimensional braided carbon fiber coated by SiC

H. J. Wang; P. Z. Gao; Z. H. Jin

doi:10.1016/j.matlet.2004.10.028

Preparation and oxidation behavior of three-dimensional braided carbon fiber coated by SiC

H. J. Wang
, P. Z. Gao
, Z. H. Jin

材料科学与工程学院

Xi'an Jiaotong University

科研成果: 期刊稿件 › 文章 › 同行评审

28 引用（Scopus）

摘要

In this paper, SiC coating on three-dimensional (3-D) braided carbon fiber was obtained, which was infiltrated with SiO₂ sol into 3-D braided carbon fiber and then carbon-thermal reduced. The effect of carbon-thermal reduction process was examined. Thermal-oxidative stability of the 3-D braided carbon fiber coated with SiC was compared with original 3-D braided carbon fiber. The oxidation stability of the SiC coating/3-D braided carbon fiber was extended up to 900-1000°C. After exposure to air at 900-1000°C, the residual weight of the composite was 26-30%.

源语言	英语
页（从-至）	486-490
页数	5
期刊	Materials Letters
卷	59
期	4
DOI	https://doi.org/10.1016/j.matlet.2004.10.028
出版状态	已出版 - 2月 2005

访问文件

10.1016/j.matlet.2004.10.028

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{d3d35b9230ed4644a5b1491c8cb5669b,

title = "Preparation and oxidation behavior of three-dimensional braided carbon fiber coated by SiC",

abstract = "In this paper, SiC coating on three-dimensional (3-D) braided carbon fiber was obtained, which was infiltrated with SiO2 sol into 3-D braided carbon fiber and then carbon-thermal reduced. The effect of carbon-thermal reduction process was examined. Thermal-oxidative stability of the 3-D braided carbon fiber coated with SiC was compared with original 3-D braided carbon fiber. The oxidation stability of the SiC coating/3-D braided carbon fiber was extended up to 900-1000°C. After exposure to air at 900-1000°C, the residual weight of the composite was 26-30\%.",

keywords = "Carbon fiber, Oxidation properties, SiC coating, Sol-dipping method",

author = "Wang, \{H. J.\} and Gao, \{P. Z.\} and Jin, \{Z. H.\}",

year = "2005",

month = feb,

doi = "10.1016/j.matlet.2004.10.028",

language = "英语",

volume = "59",

pages = "486--490",

journal = "Materials Letters",

issn = "0167-577X",

publisher = "Elsevier B.V.",

number = "4",

}

TY - JOUR

T1 - Preparation and oxidation behavior of three-dimensional braided carbon fiber coated by SiC

AU - Wang, H. J.

AU - Gao, P. Z.

AU - Jin, Z. H.

PY - 2005/2

Y1 - 2005/2

N2 - In this paper, SiC coating on three-dimensional (3-D) braided carbon fiber was obtained, which was infiltrated with SiO2 sol into 3-D braided carbon fiber and then carbon-thermal reduced. The effect of carbon-thermal reduction process was examined. Thermal-oxidative stability of the 3-D braided carbon fiber coated with SiC was compared with original 3-D braided carbon fiber. The oxidation stability of the SiC coating/3-D braided carbon fiber was extended up to 900-1000°C. After exposure to air at 900-1000°C, the residual weight of the composite was 26-30%.

AB - In this paper, SiC coating on three-dimensional (3-D) braided carbon fiber was obtained, which was infiltrated with SiO2 sol into 3-D braided carbon fiber and then carbon-thermal reduced. The effect of carbon-thermal reduction process was examined. Thermal-oxidative stability of the 3-D braided carbon fiber coated with SiC was compared with original 3-D braided carbon fiber. The oxidation stability of the SiC coating/3-D braided carbon fiber was extended up to 900-1000°C. After exposure to air at 900-1000°C, the residual weight of the composite was 26-30%.

KW - Carbon fiber

KW - Oxidation properties

KW - SiC coating

KW - Sol-dipping method

UR - https://www.scopus.com/pages/publications/9944242079

U2 - 10.1016/j.matlet.2004.10.028

DO - 10.1016/j.matlet.2004.10.028

M3 - 文章

AN - SCOPUS:9944242079

SN - 0167-577X

VL - 59

SP - 486

EP - 490

JO - Materials Letters

JF - Materials Letters

IS - 4

ER -

Preparation and oxidation behavior of three-dimensional braided carbon fiber coated by SiC

摘要

访问文件

其它文件与链接

学术指纹

引用此