Interface structure and bonding strength of brazed joint of TiC cermet/steel

Ji Cai Feng; Xiang Meng Jing; Li Xia Zhang; Hong Liu

Interface structure and bonding strength of brazed joint of TiC cermet/steel

Ji Cai Feng
, Xiang Meng Jing
, Li Xia Zhang
, Hong Liu

Harbin Institute of Technology

科研成果: 期刊稿件 › 文章 › 同行评审

3 引用（Scopus）

摘要

The vacuum brazing of TiC cermet (synthesized by SHS) to medium carbon steel was carried out with BAg45CuZn brazing filler metal, and the interface structure and shear strength of the joints were also investigated by means of SEM, EPMA and XRD. The experimental results showed that the bonding of TiC cermet to medium steel can be performed with BAg45CuZn filler metal. The interface structure of the joint is TiC cermet/(Cu, Ni)/Ag(s, s) + Cu(s, s)/(Cu, Ni)/(Cu, Ni) + (Fe, Ni)/medium carbon steel. The maximum shear strength of the joint brazed at 850°C for 10 min is up to 121 MPa at room temperature.

源语言	英语
页（从-至）	5-8
页数	4
期刊	Hanjie Xuebao/Transactions of the China Welding Institution
卷	27
期	1
出版状态	已出版 - 1月 2006
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{2e2f15be07f34ecf857dc19c6c6dd2b6,

title = "Interface structure and bonding strength of brazed joint of TiC cermet/steel",

abstract = "The vacuum brazing of TiC cermet (synthesized by SHS) to medium carbon steel was carried out with BAg45CuZn brazing filler metal, and the interface structure and shear strength of the joints were also investigated by means of SEM, EPMA and XRD. The experimental results showed that the bonding of TiC cermet to medium steel can be performed with BAg45CuZn filler metal. The interface structure of the joint is TiC cermet/(Cu, Ni)/Ag(s, s) + Cu(s, s)/(Cu, Ni)/(Cu, Ni) + (Fe, Ni)/medium carbon steel. The maximum shear strength of the joint brazed at 850°C for 10 min is up to 121 MPa at room temperature.",

keywords = "Bonding strength, Interface structure, Steel, TiC cermet, Vacuum brazing",

author = "Feng, \{Ji Cai\} and Jing, \{Xiang Meng\} and Zhang, \{Li Xia\} and Hong Liu",

year = "2006",

month = jan,

language = "英语",

volume = "27",

pages = "5--8",

journal = "Hanjie Xuebao/Transactions of the China Welding Institution",

issn = "0253-360X",

publisher = "Harbin Research Institute of Welding",

number = "1",

}

TY - JOUR

T1 - Interface structure and bonding strength of brazed joint of TiC cermet/steel

AU - Feng, Ji Cai

AU - Jing, Xiang Meng

AU - Zhang, Li Xia

AU - Liu, Hong

PY - 2006/1

Y1 - 2006/1

N2 - The vacuum brazing of TiC cermet (synthesized by SHS) to medium carbon steel was carried out with BAg45CuZn brazing filler metal, and the interface structure and shear strength of the joints were also investigated by means of SEM, EPMA and XRD. The experimental results showed that the bonding of TiC cermet to medium steel can be performed with BAg45CuZn filler metal. The interface structure of the joint is TiC cermet/(Cu, Ni)/Ag(s, s) + Cu(s, s)/(Cu, Ni)/(Cu, Ni) + (Fe, Ni)/medium carbon steel. The maximum shear strength of the joint brazed at 850°C for 10 min is up to 121 MPa at room temperature.

AB - The vacuum brazing of TiC cermet (synthesized by SHS) to medium carbon steel was carried out with BAg45CuZn brazing filler metal, and the interface structure and shear strength of the joints were also investigated by means of SEM, EPMA and XRD. The experimental results showed that the bonding of TiC cermet to medium steel can be performed with BAg45CuZn filler metal. The interface structure of the joint is TiC cermet/(Cu, Ni)/Ag(s, s) + Cu(s, s)/(Cu, Ni)/(Cu, Ni) + (Fe, Ni)/medium carbon steel. The maximum shear strength of the joint brazed at 850°C for 10 min is up to 121 MPa at room temperature.

KW - Bonding strength

KW - Interface structure

KW - Steel

KW - TiC cermet

KW - Vacuum brazing

UR - https://www.scopus.com/pages/publications/33645907227

M3 - 文章

AN - SCOPUS:33645907227

SN - 0253-360X

VL - 27

SP - 5

EP - 8

JO - Hanjie Xuebao/Transactions of the China Welding Institution

JF - Hanjie Xuebao/Transactions of the China Welding Institution

IS - 1

ER -

Interface structure and bonding strength of brazed joint of TiC cermet/steel

摘要

其它文件与链接

学术指纹

引用此