title = "Improvement on dielectric properties of CaCu3Ti4O12 ceramics by heat treatment in rich oxygen atmosphere",
abstract = "CaCu3Ti4O12 ceramics were synthesized by using the solid-state reaction method, and the roles of the heat treatment on the microstructure and dielectric properties were investigated. It is indicated that no second phase is found after heat treatment. At room temperature, the dielectric constant is decreased slightly and the dielectric loss tangent is effectively suppressed to 0.03-0.04. In the temperature range of 183-273 K, the dielectric loss of CaCu3Ti4O12 ceramics is composed of conductance loss at low frequency and two relaxation loss peaks at high frequency. It is worth noting that the conductance loss at low frequency is reduced apparently by the heat treatment. Furthermore, the results of J-E exhibit that the breakdown field and nonlinear coefficient of CaCu3Ti4O12 ceramics are increased from 226 V/mm and 3.52 to 397 V/mm and 4.51, respectively. The Schottky barrier height of CCTO ceramics is boosted from 0.56 eV to 0.63 eV.",
keywords = "Breakdown field, CaCuTiO, Dielectric loss, Oxidizing atmosphere",
author = "Xuetong Zhao and Shuai Li and Ruijin Liao and Junyan Zhang and Feipeng Wang and Jianying Li",
note = "Publisher Copyright: {\textcopyright} 2015 IEEE.; IEEE Conference on Electrical Insulation and Dielectric Phenomena, CEIDP 2015 ; Conference date: 18-10-2015 Through 21-10-2015",
year = "2015",
month = dec,
day = "9",
doi = "10.1109/CEIDP.2015.7352002",
language = "英语",
series = "Annual Report - Conference on Electrical Insulation and Dielectric Phenomena, CEIDP",
publisher = "Institute of Electrical and Electronics Engineers Inc.",
pages = "76--79",
booktitle = "2015 IEEE Conference on Electrical Insulation and Dielectric Phenomena, CEIDP 2015",
}