Enhancement of thermal shock resistance in β-Si₃N₄ coating with in situ synthesized β-Si₃N₄ nanowires/nanobelts on porous Si₃N₄ ceramics

A dense β-Si₃N₄ coating toughened by β-Si₃N₄ nanowires/nanobelts was prepared by a combined technique involving chemical vapor deposition and reactive melt infiltration to protect porous Si₃N₄ ceramics in this work. A porous β-Si₃N₄ nanowires/nanobelts layer was synthesized in situ on porous Si₃N₄ ceramics by chemical vapor deposition, and then Y–Si–Al–O–N silicate liquid was infiltrated into the porous layer by reactive melt infiltration to form a dense composite coating. The coating consisted of well-dispersion β-Si₃N₄ nanowires/nanobelts, fine β-Si₃N₄ particles and small amount of silicate glass. The testing results revealed that as-prepared coating displayed a relatively high fracture toughness, which was up to 7.9 ± 0.05 MPa m^1/2, and it is of great significance to improve thermal shock resistance of the coating. After thermal cycling for 15 times at ΔT = 1200 °C, the coated porous Si₃N₄ ceramics still had a high residual strength ratio of 82.2%, and its water absorption increased only to 6.21% from 3.47%. The results will be a solid foundation for the application of the coating in long-period extreme high temperature environment.