T1 - Effects of temperature gradient on space charge accumulation at applied voltage reversal in LDPE film
AU - Wu, Kai
AU - Chen, Xi
AU - Wang, Xia
AU - Wang, Zengbin
AU - Cheng, Yonghong
AU - Peng, Zongren
PY - 2010
Y1 - 2010
N2 - Temperature gradient through the cable thickness occurs due to Joule heat arising from the electric current in the high voltage cable conductor, and affects the injection and migration of charge, leading to the insulation failure while a sudden power off or polarity reversal takes place due to the charge accumulation. In this article, based on the PEA (pulsed electroacoustic) method, the space charge accumulation and maximum transient electric field distortion during polarity reversal were studied under the different temperature gradient and a direct current stress of 50kV/mm. The experimental results show that the maximum steady-state electric field was measured near the low temperature electrode, but the maximum transient electric field could appear near the high temperature electrode.
AB - Temperature gradient through the cable thickness occurs due to Joule heat arising from the electric current in the high voltage cable conductor, and affects the injection and migration of charge, leading to the insulation failure while a sudden power off or polarity reversal takes place due to the charge accumulation. In this article, based on the PEA (pulsed electroacoustic) method, the space charge accumulation and maximum transient electric field distortion during polarity reversal were studied under the different temperature gradient and a direct current stress of 50kV/mm. The experimental results show that the maximum steady-state electric field was measured near the low temperature electrode, but the maximum transient electric field could appear near the high temperature electrode.
KW - LDPE
KW - Space charge
KW - Temperature gradient
KW - Transient electric field
KW - Voltage polarity reversal
UR - https://www.scopus.com/pages/publications/77958034833
U2 - 10.1109/ICSD.2010.5568030
DO - 10.1109/ICSD.2010.5568030
M3 - 会议稿件
AN - SCOPUS:77958034833
SN - 9781424479443
T3 - Proceedings of the 2010 IEEE International Conference on Solid Dielectrics, ICSD 2010
BT - Proceedings of the 2010 IEEE International Conference on Solid Dielectrics, ICSD 2010
T2 - 2010 IEEE International Conference on Solid Dielectrics, ICSD 2010
Y2 - 4 July 2010 through 9 July 2010
ER -