T1 - Effect and mechanism analysis of matrix resin type on thermal aging characteristics of semi-conductive shielding material for high voltage cable
AU - Liu, Tianyao
AU - Liu, Tianzhen
AU - Li, Xuejing
AU - Wei, Yanhui
AU - Zhu, Yuanwei
AU - He, Jinliang
AU - Li, Guochang
N1 - Publisher Copyright:
© 2024 Wiley Periodicals LLC.
PY - 2024/5/10
Y1 - 2024/5/10
N2 - The type of matrix resin of the semi-conductive shielding layer directly affects the thermal aging characteristics of the semi-conductive shielding layer and the high-voltage cable. In this paper, ethylene vinyl acetate (EVA), ethylene ethyl acrylate (EEA), and ethylene butyl acrylate (EBA) resins were used as matrix to prepare carbon black (CB) + EVA, CB + EEA, and CB + EBA shielding materials. The law of physicochemical, electrical, and mechanical properties of different matrix resin shielding materials with aging time was studied, and the influence mechanism of matrix resin on the aging characteristics of shielding materials was analyzed. The results show: with the increase of aging time, the crystallization area and the number of functional groups of the three shielding materials decreased to varying degrees. The number of functional groups in CB + EBA shielding materials decreased evenly with aging time, but that of CB + EVA and CB + EEA shielding materials changed significantly after 7 days of aging. After 60 days of aging, the crystallization area of CB + EBA shielding material changed slightly, but that of CB + EVA and CB + EEA shielding material decrease significantly. The electrical properties of the three shielding materials showed different decreasing trend with aging time. When the aging time is 7 days, the positive temperature coefficient (PTC) effect of CB + EEA shielding material decreases obviously. When the aging time is 30 days, the resistivity of CB + EVA and CB + EEA shielding material increases slowly (9 Ω cm–12 Ω cm) with the increase of temperature. When the aging time is 60 days, the resistivity of CB + EBA shielding material decreases obviously, and the PTC effect weakens obviously. Taking the mechanical properties of the shielding material as reference, the rapid deterioration stage of the mechanical properties of the three shielding materials is different. The CB + EVA and CB + EEA shielding material rapid deterioration time is 0–7 days, and the tensile strength and elongation of the shielding material are greatly reduced. The rapid deterioration stage of CB + EBA shielding material is 7–30 days, and the tensile strength and elongation decrease from 24.38 MPa and 499.5% to 14 MPa and 155.7%, respectively. This work can provide data support for the selection of matrix resin of shielding material and the fault analysis of shielding layer of high voltage cable.
AB - The type of matrix resin of the semi-conductive shielding layer directly affects the thermal aging characteristics of the semi-conductive shielding layer and the high-voltage cable. In this paper, ethylene vinyl acetate (EVA), ethylene ethyl acrylate (EEA), and ethylene butyl acrylate (EBA) resins were used as matrix to prepare carbon black (CB) + EVA, CB + EEA, and CB + EBA shielding materials. The law of physicochemical, electrical, and mechanical properties of different matrix resin shielding materials with aging time was studied, and the influence mechanism of matrix resin on the aging characteristics of shielding materials was analyzed. The results show: with the increase of aging time, the crystallization area and the number of functional groups of the three shielding materials decreased to varying degrees. The number of functional groups in CB + EBA shielding materials decreased evenly with aging time, but that of CB + EVA and CB + EEA shielding materials changed significantly after 7 days of aging. After 60 days of aging, the crystallization area of CB + EBA shielding material changed slightly, but that of CB + EVA and CB + EEA shielding material decrease significantly. The electrical properties of the three shielding materials showed different decreasing trend with aging time. When the aging time is 7 days, the positive temperature coefficient (PTC) effect of CB + EEA shielding material decreases obviously. When the aging time is 30 days, the resistivity of CB + EVA and CB + EEA shielding material increases slowly (9 Ω cm–12 Ω cm) with the increase of temperature. When the aging time is 60 days, the resistivity of CB + EBA shielding material decreases obviously, and the PTC effect weakens obviously. Taking the mechanical properties of the shielding material as reference, the rapid deterioration stage of the mechanical properties of the three shielding materials is different. The CB + EVA and CB + EEA shielding material rapid deterioration time is 0–7 days, and the tensile strength and elongation of the shielding material are greatly reduced. The rapid deterioration stage of CB + EBA shielding material is 7–30 days, and the tensile strength and elongation decrease from 24.38 MPa and 499.5% to 14 MPa and 155.7%, respectively. This work can provide data support for the selection of matrix resin of shielding material and the fault analysis of shielding layer of high voltage cable.
KW - high voltage cable
KW - matrix resin type
KW - semi-conductive shielding layer
KW - thermo-oxidative aging mechanisms
UR - https://www.scopus.com/pages/publications/85186257065
U2 - 10.1002/app.55311
DO - 10.1002/app.55311
M3 - 文章
AN - SCOPUS:85186257065
SN - 0021-8995
VL - 141
JO - Journal of Applied Polymer Science
JF - Journal of Applied Polymer Science
IS - 18
M1 - e55311
ER -