Corrosion behavior of Sc2O3–Y2O3 co-stabilized ZrO2 thermal barrier coatings with CMAS attack

W. Fan; Y. Bai; Y. F. Liu; Y. X. Kang; Y. Wang; Z. Z. Wang; W. Z. Tao

doi:10.1016/j.ceramint.2019.05.063

Corrosion behavior of Sc₂O₃–Y₂O₃ co-stabilized ZrO₂ thermal barrier coatings with CMAS attack

W. Fan
, Y. Bai
, Y. F. Liu
, Y. X. Kang
, Y. Wang
, Z. Z. Wang
, W. Z. Tao

材料科学与工程学院

Xi'an Jiaotong University
Jiangsu Lida Hi-Tech Special Material Co., Ltd

科研成果: 期刊稿件 › 文章 › 同行评审

69 引用（Scopus）

摘要

Traditional viewpoints state that defects, such as pores or cracks, that generally exist in plasma sprayed thermal barrier coatings (TBCs) can provide fast infiltration channels for molten calcia-magnesia-alumino-silicate (CMAS). In contrast with this viewpoint, results from this study suggest that the effect of defects on the CMAS infiltration of the yttria stabilized zirconia (YSZ) coating is limited, even though the dense YSZ bulk material still cannot inhibit the infiltration of CMAS. However, a few additions of Sc₂O₃ can significantly improve the CMAS resistance of the YSZ coating owing to the lower solubility of Sc³⁺ in the CMAS. Our findings provide key insights for the development of CMAS-resistant TBCs.

源语言	英语
页（从-至）	15763-15767
页数	5
期刊	Ceramics International
卷	45
期	12
DOI	https://doi.org/10.1016/j.ceramint.2019.05.063
出版状态	已出版 - 15 8月 2019

访问文件

10.1016/j.ceramint.2019.05.063

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{410eebadb64a4a21a2d47fe8d5f7fc92,

title = "Corrosion behavior of Sc2O3{\textendash}Y2O3 co-stabilized ZrO2 thermal barrier coatings with CMAS attack",

abstract = "Traditional viewpoints state that defects, such as pores or cracks, that generally exist in plasma sprayed thermal barrier coatings (TBCs) can provide fast infiltration channels for molten calcia-magnesia-alumino-silicate (CMAS). In contrast with this viewpoint, results from this study suggest that the effect of defects on the CMAS infiltration of the yttria stabilized zirconia (YSZ) coating is limited, even though the dense YSZ bulk material still cannot inhibit the infiltration of CMAS. However, a few additions of Sc2O3 can significantly improve the CMAS resistance of the YSZ coating owing to the lower solubility of Sc3+ in the CMAS. Our findings provide key insights for the development of CMAS-resistant TBCs.",

keywords = "CMAS, Corrosion, ScO{\textendash}YO{\textendash}ZrO, Thermal barrier coating",

author = "W. Fan and Y. Bai and Liu, \{Y. F.\} and Kang, \{Y. X.\} and Y. Wang and Wang, \{Z. Z.\} and Tao, \{W. Z.\}",

note = "Publisher Copyright: {\textcopyright} 2019 Elsevier Ltd and Techna Group S.r.l.",

year = "2019",

month = aug,

day = "15",

doi = "10.1016/j.ceramint.2019.05.063",

language = "英语",

volume = "45",

pages = "15763--15767",

journal = "Ceramics International",

issn = "0272-8842",

publisher = "Elsevier Ltd",

number = "12",

}

TY - JOUR

T1 - Corrosion behavior of Sc2O3–Y2O3 co-stabilized ZrO2 thermal barrier coatings with CMAS attack

AU - Fan, W.

AU - Bai, Y.

AU - Liu, Y. F.

AU - Kang, Y. X.

AU - Wang, Y.

AU - Wang, Z. Z.

AU - Tao, W. Z.

PY - 2019/8/15

Y1 - 2019/8/15

N2 - Traditional viewpoints state that defects, such as pores or cracks, that generally exist in plasma sprayed thermal barrier coatings (TBCs) can provide fast infiltration channels for molten calcia-magnesia-alumino-silicate (CMAS). In contrast with this viewpoint, results from this study suggest that the effect of defects on the CMAS infiltration of the yttria stabilized zirconia (YSZ) coating is limited, even though the dense YSZ bulk material still cannot inhibit the infiltration of CMAS. However, a few additions of Sc2O3 can significantly improve the CMAS resistance of the YSZ coating owing to the lower solubility of Sc3+ in the CMAS. Our findings provide key insights for the development of CMAS-resistant TBCs.

AB - Traditional viewpoints state that defects, such as pores or cracks, that generally exist in plasma sprayed thermal barrier coatings (TBCs) can provide fast infiltration channels for molten calcia-magnesia-alumino-silicate (CMAS). In contrast with this viewpoint, results from this study suggest that the effect of defects on the CMAS infiltration of the yttria stabilized zirconia (YSZ) coating is limited, even though the dense YSZ bulk material still cannot inhibit the infiltration of CMAS. However, a few additions of Sc2O3 can significantly improve the CMAS resistance of the YSZ coating owing to the lower solubility of Sc3+ in the CMAS. Our findings provide key insights for the development of CMAS-resistant TBCs.

KW - CMAS

KW - Corrosion

KW - ScO–YO–ZrO

KW - Thermal barrier coating

UR - https://www.scopus.com/pages/publications/85065591418

U2 - 10.1016/j.ceramint.2019.05.063

DO - 10.1016/j.ceramint.2019.05.063

M3 - 文章

AN - SCOPUS:85065591418

SN - 0272-8842

VL - 45

SP - 15763

EP - 15767

JO - Ceramics International

JF - Ceramics International

IS - 12

ER -

Corrosion behavior of Sc2O3–Y2O3 co-stabilized ZrO2 thermal barrier coatings with CMAS attack

摘要

访问文件

其它文件与链接

学术指纹

引用此

Corrosion behavior of Sc₂O₃–Y₂O₃ co-stabilized ZrO₂ thermal barrier coatings with CMAS attack