Characterization and piezoelectric thermal stability of PIN-PMN-PT ternary ceramics near the morphotropic phase boundary

Dabin Lin; Zhenrong Li; Fei Li; Zhuo Xu; Xi Yao

doi:10.1016/j.jallcom.2009.09.026

Characterization and piezoelectric thermal stability of PIN-PMN-PT ternary ceramics near the morphotropic phase boundary

Dabin Lin
, Zhenrong Li
, Fei Li
, Zhuo Xu
, Xi Yao

Key Lab of the Ministry of Education for Process Control and Efficiency Egineering

科研成果: 期刊稿件 › 文章 › 同行评审

108 引用（Scopus）

摘要

The phase structure and piezo/dielectric properties of xPb(In_1/2Nb_1/2)O₃-yPb(Mg_1/3Nb_2/3)O₃-zPbTiO₃ (PIN-PMN-PT x/y/z) ternary ceramics with morphotropic phase boundary (MPB) composition were investigated. It was found that Curie temperatures of choosing composition changed from 165 °C to 293 °C and the piezoelectric properties are almost the same at room temperature in PIN-PMN-PT system near MPB. The piezoelectric coefficient d₃₃ and electromechanical coupling factor k_p are higher than 440 pC/N and 60%, respectively. Temperautre and dc bias dependence of piezoelectric response for PIN-PMN-PT ceramics were measured. The usage temperature range was found to be improved, compared with PMN-PT single crystal near MPB.

源语言	英语
页（从-至）	115-118
页数	4
期刊	Journal of Alloys and Compounds
卷	489
期	1
DOI	https://doi.org/10.1016/j.jallcom.2009.09.026
出版状态	已出版 - 7 1月 2010
已对外发布	是

访问文件

10.1016/j.jallcom.2009.09.026

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{e66235809d6443f682c6a3ee3ab8ed69,

title = "Characterization and piezoelectric thermal stability of PIN-PMN-PT ternary ceramics near the morphotropic phase boundary",

abstract = "The phase structure and piezo/dielectric properties of xPb(In1/2Nb1/2)O3-yPb(Mg1/3Nb2/3)O3-zPbTiO3 (PIN-PMN-PT x/y/z) ternary ceramics with morphotropic phase boundary (MPB) composition were investigated. It was found that Curie temperatures of choosing composition changed from 165 °C to 293 °C and the piezoelectric properties are almost the same at room temperature in PIN-PMN-PT system near MPB. The piezoelectric coefficient d33 and electromechanical coupling factor kp are higher than 440 pC/N and 60\%, respectively. Temperautre and dc bias dependence of piezoelectric response for PIN-PMN-PT ceramics were measured. The usage temperature range was found to be improved, compared with PMN-PT single crystal near MPB.",

keywords = "Curie temperature, Ferroelectrics, Morphotropic phase boundary, Piezoelectric ceramics",

author = "Dabin Lin and Zhenrong Li and Fei Li and Zhuo Xu and Xi Yao",

year = "2010",

month = jan,

day = "7",

doi = "10.1016/j.jallcom.2009.09.026",

language = "英语",

volume = "489",

pages = "115--118",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

number = "1",

}

TY - JOUR

T1 - Characterization and piezoelectric thermal stability of PIN-PMN-PT ternary ceramics near the morphotropic phase boundary

AU - Lin, Dabin

AU - Li, Zhenrong

AU - Li, Fei

AU - Xu, Zhuo

AU - Yao, Xi

PY - 2010/1/7

Y1 - 2010/1/7

N2 - The phase structure and piezo/dielectric properties of xPb(In1/2Nb1/2)O3-yPb(Mg1/3Nb2/3)O3-zPbTiO3 (PIN-PMN-PT x/y/z) ternary ceramics with morphotropic phase boundary (MPB) composition were investigated. It was found that Curie temperatures of choosing composition changed from 165 °C to 293 °C and the piezoelectric properties are almost the same at room temperature in PIN-PMN-PT system near MPB. The piezoelectric coefficient d33 and electromechanical coupling factor kp are higher than 440 pC/N and 60%, respectively. Temperautre and dc bias dependence of piezoelectric response for PIN-PMN-PT ceramics were measured. The usage temperature range was found to be improved, compared with PMN-PT single crystal near MPB.

AB - The phase structure and piezo/dielectric properties of xPb(In1/2Nb1/2)O3-yPb(Mg1/3Nb2/3)O3-zPbTiO3 (PIN-PMN-PT x/y/z) ternary ceramics with morphotropic phase boundary (MPB) composition were investigated. It was found that Curie temperatures of choosing composition changed from 165 °C to 293 °C and the piezoelectric properties are almost the same at room temperature in PIN-PMN-PT system near MPB. The piezoelectric coefficient d33 and electromechanical coupling factor kp are higher than 440 pC/N and 60%, respectively. Temperautre and dc bias dependence of piezoelectric response for PIN-PMN-PT ceramics were measured. The usage temperature range was found to be improved, compared with PMN-PT single crystal near MPB.

KW - Curie temperature

KW - Ferroelectrics

KW - Morphotropic phase boundary

KW - Piezoelectric ceramics

UR - https://www.scopus.com/pages/publications/70649105481

U2 - 10.1016/j.jallcom.2009.09.026

DO - 10.1016/j.jallcom.2009.09.026

M3 - 文章

AN - SCOPUS:70649105481

SN - 0925-8388

VL - 489

SP - 115

EP - 118

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

IS - 1

ER -

Characterization and piezoelectric thermal stability of PIN-PMN-PT ternary ceramics near the morphotropic phase boundary

摘要

访问文件

其它文件与链接

学术指纹

引用此