A new strategy to inhibit stray grain formation during laser directed solidification of single crystal superalloys

  • Jiawei Wang
  • , Huaming Wang
  • , Kangjie Li
  • , Mingyuan Chen
  • , Meiling Zhang
  • , Bo Zhang
  • , Jingwei Yuan
  • , Xu Cheng
  • , Shuquan Zhang
  • , Yudai Wang
  • Beihang University
  • National Engineering Laboratory of Additive Manufacturing for Large Metallic Components

科研成果: 期刊稿件文章同行评审

15 引用 (Scopus)

摘要

Although laser surface remelting displays excellent potential for repairing the nickel-based single crystal (SX) superalloy components, controlling the grain structure while avoiding the stray grain (SG) formation is still a challenge in the industry. In order to inhibit SG formation for nickel superalloys, a novel rotated laser irradiation approach is introduced in this paper and the study of the origin of the SG formation in laser directed solidification process. Besides, a numerical model of combined alloy composition with the tendency of equiaxed grain formation during epitaxial growth processing was developed in this paper to reveal the mechanism of SG formation at the bottom of the molten pool. Results indicate that SGs formed at the bottom of the molten pool are mainly due to the remarkably increased possibility of the equiaxed grain transformation with the rough fusion interface. During the laser process, the number of SGs gradually decreases with the increase of the angle (θ) between the laser irradiation and gravity direction. For θ = 90°, well-aligned epitaxial growth of [001] dendrites without any SGs are observed in the pool with the smooth fusion interface. Furthermore, applying the new laser deposition technique based on this phenomenon during laser directional solidification will be an effective method to control the grain-oriented growth in industrial manufacture for the single crystal components.

源语言英语
期刊论文编号163852
期刊Journal of Alloys and Compounds
906
DOI
出版状态已出版 - 15 6月 2022
已对外发布

学术指纹

探究 'A new strategy to inhibit stray grain formation during laser directed solidification of single crystal superalloys' 的科研主题。它们共同构成独一无二的学术指纹。

引用此