A long-term ultrahigh temperature application of layered silicide coated Nb alloy in air

Jia Sun; Qian Gang Fu; Tao Li; Chen Wang; Cai Xia Huo; Hong Zhou; Guan Jun Yang; Le Sun

doi:10.1016/j.apsusc.2018.01.114

A long-term ultrahigh temperature application of layered silicide coated Nb alloy in air

Jia Sun
, Qian Gang Fu
, Tao Li
, Chen Wang
, Cai Xia Huo
, Hong Zhou
, Guan Jun Yang
, Le Sun

材料科学与工程学院

Northwestern Polytechnical University Xian
Technische Universität Darmstadt

科研成果: 期刊稿件 › 文章 › 同行评审

32 引用（Scopus）

摘要

Nb-based alloy possessed limited application service life at ultrahigh temperature (>1400 °C) in air even taking the effective protective coating strategy into consideration for last decades. In this work a long duration of above 128 h at 1500 °C in air was successfully achieved on Nb-based alloy thanked to multi-layered silicide coating. Through optimizing interfaces, the MoSi ₂ /NbSi ₂ silicide coating with Al ₂ O ₃ -adsorbed-particles layer exhibited three-times higher of oxidation resistance capacity than the one without it. In MoSi ₂ -Al ₂ O ₃ -NbSi ₂ multilayer coating, the Al ₂ O ₃ -adsorbed-particles layer playing as an element-diffusion barrier role, as well as the formed porous Nb ₅ Si ₃ layer as a stress transition zone, contributed to the significant improvement.

源语言	英语
页（从-至）	1111-1118
页数	8
期刊	Applied Surface Science
卷	439
DOI	https://doi.org/10.1016/j.apsusc.2018.01.114
出版状态	已出版 - 1 5月 2018

访问文件

10.1016/j.apsusc.2018.01.114

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{194d2eeaa7184e2bba2a16d3a067b74c,

title = "A long-term ultrahigh temperature application of layered silicide coated Nb alloy in air",

abstract = " Nb-based alloy possessed limited application service life at ultrahigh temperature (>1400 °C) in air even taking the effective protective coating strategy into consideration for last decades. In this work a long duration of above 128 h at 1500 °C in air was successfully achieved on Nb-based alloy thanked to multi-layered silicide coating. Through optimizing interfaces, the MoSi 2 /NbSi 2 silicide coating with Al 2 O 3 -adsorbed-particles layer exhibited three-times higher of oxidation resistance capacity than the one without it. In MoSi 2 -Al 2 O 3 -NbSi 2 multilayer coating, the Al 2 O 3 -adsorbed-particles layer playing as an element-diffusion barrier role, as well as the formed porous Nb 5 Si 3 layer as a stress transition zone, contributed to the significant improvement.",

keywords = "Coatings, Diffusion, Molybdenum silicide, Oxidation resistance",

author = "Jia Sun and Fu, \{Qian Gang\} and Tao Li and Chen Wang and Huo, \{Cai Xia\} and Hong Zhou and Yang, \{Guan Jun\} and Le Sun",

note = "Publisher Copyright: {\textcopyright} 2018",

year = "2018",

month = may,

day = "1",

doi = "10.1016/j.apsusc.2018.01.114",

language = "英语",

volume = "439",

pages = "1111--1118",

journal = "Applied Surface Science",

issn = "0169-4332",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - A long-term ultrahigh temperature application of layered silicide coated Nb alloy in air

AU - Sun, Jia

AU - Fu, Qian Gang

AU - Li, Tao

AU - Wang, Chen

AU - Huo, Cai Xia

AU - Zhou, Hong

AU - Yang, Guan Jun

AU - Sun, Le

PY - 2018/5/1

Y1 - 2018/5/1

N2 - Nb-based alloy possessed limited application service life at ultrahigh temperature (>1400 °C) in air even taking the effective protective coating strategy into consideration for last decades. In this work a long duration of above 128 h at 1500 °C in air was successfully achieved on Nb-based alloy thanked to multi-layered silicide coating. Through optimizing interfaces, the MoSi 2 /NbSi 2 silicide coating with Al 2 O 3 -adsorbed-particles layer exhibited three-times higher of oxidation resistance capacity than the one without it. In MoSi 2 -Al 2 O 3 -NbSi 2 multilayer coating, the Al 2 O 3 -adsorbed-particles layer playing as an element-diffusion barrier role, as well as the formed porous Nb 5 Si 3 layer as a stress transition zone, contributed to the significant improvement.

AB - Nb-based alloy possessed limited application service life at ultrahigh temperature (>1400 °C) in air even taking the effective protective coating strategy into consideration for last decades. In this work a long duration of above 128 h at 1500 °C in air was successfully achieved on Nb-based alloy thanked to multi-layered silicide coating. Through optimizing interfaces, the MoSi 2 /NbSi 2 silicide coating with Al 2 O 3 -adsorbed-particles layer exhibited three-times higher of oxidation resistance capacity than the one without it. In MoSi 2 -Al 2 O 3 -NbSi 2 multilayer coating, the Al 2 O 3 -adsorbed-particles layer playing as an element-diffusion barrier role, as well as the formed porous Nb 5 Si 3 layer as a stress transition zone, contributed to the significant improvement.

KW - Coatings

KW - Diffusion

KW - Molybdenum silicide

KW - Oxidation resistance

UR - https://www.scopus.com/pages/publications/85041378552

U2 - 10.1016/j.apsusc.2018.01.114

DO - 10.1016/j.apsusc.2018.01.114

M3 - 文章

AN - SCOPUS:85041378552

SN - 0169-4332

VL - 439

SP - 1111

EP - 1118

JO - Applied Surface Science

JF - Applied Surface Science

ER -

A long-term ultrahigh temperature application of layered silicide coated Nb alloy in air

摘要

访问文件

其它文件与链接

学术指纹

引用此