Thermal annealing and single-domain preparation in tetragonal Pb(In_1/2Nb_1/2)O₃-Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ crystal for electro-optic and non-linear optical applications

The relaxor-PbTiO₃ single crystal has attracted extensive attention in ultrasound transducers, sensors, actuators, and optoelectronics devices due to its excellent piezoelectric response and electro-optic properties. Preparation of a single-domain crystal as a critical process for application in electro-optic and non-linear optical devices suffers from serious and inevitable cracking. Therefore, a pre-poling thermal annealing process was suggested to release residual stress from crystal growth and the ferroelectric-paraelectric phase transition, which significantly reduced the chance of cracking. The effect of thermal annealing on dielectric properties, strain behavior, and domain structure were investigated. As a result, a significant increase of the dielectric constant near room temperature was obtained after annealing, which is close to the dielectric constant of the a-oriented domain. The annealed single crystal showed a lower and sharper strain peak at the coercive electric field compared with the unannealed sample, and the 90° domain walls completely vanished, which was verified by optical microscopy. The crack-free single-domain crystal showed excellent optical quality, with high transmittance of approximately 70% in the visible and near-infrared regions, which indicates that this crystal is a promising candidate for applications in electro-optic and non-linear optical devices.