Structure and properties of Bi(Zn_½Ti_½)O₃-modified Pb(Zr,Ti)O₃ piezo-/ferroelectric ceramics around the ternary morphotropic phase boundary

To develop high-performance piezo-/ferroelectric materials, Bi(Zn_½Ti_½)O₃–PbZrO₃–PbTiO₃ (BZT–PZ–PT) ternary solid solution with compositions around the morphotropic phase boundary (MPB) is synthesized by solid-state reaction. The crystal structure and electric properties are investigated systematically by X-ray powder diffraction (XRD), dielectric spectroscopy, and ferroelectric and piezoelectric measurements. On the basis of the results of the XRD, dielectric and ferroelectric measurements, the pseudo-binary phase diagram of the yBi(Zn_½Ti_½)O₃–(1 − y)[(1 − x)PbZrO₃–xPbTiO₃] system has been constructed for three series, namely, y = 0.05, 0.10, and 0.15. It is found that the introduction of BZT into the PZT system makes the paraelectric to ferroelectric phase transition more diffuse, brings the MPB to a lower PT content, and enlarges the MPB region. The best properties with an improved dielectric constant ε' = 1248, and a large remnant polarization P_r = 33 μC/cm², as well as a relatively high T_C = 286°C, and a high coercive field E_c = 23 kV/cm was achieved in the y = 0.15 series with MPB composition x = 0.425, making it a promising material for high-power piezoelectric applications.