Structure and microwave dielectric properties of Bi _1.5Zn _1.0Nb _1.5O ₇ thin films deposited on alumina substrates by pulsed laser deposition

Bi _1.5Zn _1.0Nb _1.5O ₇ (BZN) thin films were deposited on polycrystalline alumina substrates by pulsed laser deposition at different substrate temperatures. The phase structure and surface morphology were characterized using X-ray diffractometer (XRD) and atomic force microscopy. Microwave dielectric properties were performed using split-post dielectric resonator method at spot frequencies of 10, 15 and 19 GHz, respectively. The XRD results indicate that the as-deposited Bi _1.5Zn _1.0Nb _1.5O ₇ thin films deposited at 650°C are amorphous in nature. The dielectric permittivity and loss tangent of the amorphous BZN thin films are 75.5 and 0.013 at 10 GHz, respectively. As the measure frequency increased to 19 GHz, the dielectric permittivity slightly decreases and loss tangent slightly increases. BZN thin films were crystallized after the post-annealing by a rapid thermal annealing in air for 30 min. The crystallized BZN thin films exhibit the excellent dielectric properties and frequency responses. The dielectric permittivity and loss tangent of the crystallized BZN thin films are 154 and 0.038 at 10 GHz, respectively.