Solar fuel production at high temperatures using ceria as a dense membrane

In this paper, ceria was proposed as a candidate material of membrane reactor for solar fuel production. A thermodynamic model of the membrane reactor system based on ceria with heat recovery was established and solar-to-fuel efficiency of both inert gas-assisted and pump-assisted CO₂ splitting was calculated under a broad range of conditions. For system using inert gas, gas heat recovery is the determining factor for energy conversion efficiency. The energy efficiency is calculated to be >10% at 1800 K when the oxygen pressure at the inlet of reduction zone is lower than 10^-6MPa. Increase of total pressure of the oxidation zone could improve the energy efficiency due to decrease of gas heat loss. Significant promotion in efficiency could be expected when a pump is applied to avoid using inert gas. Solar-to-fuel efficiency could be above 40% assuming good heat recovery. For the membrane reactor with a pump applied to maintain a vacuum atmosphere of the reduction zone, a simplified steady state model was put forward to predict the converting process and estimate the productivity. The diffusion rate of oxygen ions in the membrane is fast enough for conversion of considerable amount of CO₂ in the reactor with a limited geometry.