Preparation, characterization and photocatalytic activities of holmium-doped titanium dioxide nanoparticles

Holmium-doped TiO₂ nanoparticles with high photocatalytic activities were prepared by sol-gel method and characterized by X-ray diffraction, transmission electron microscopy, ultraviolet-visible diffuse reflectance spectroscopy, and surface area measurement by nitrogen adsorption in this study. Experimental results indicated holmium doping could increase the surface area of TiO₂ nanoparticles, and inhibit the growth of crystalline size and the anatase-to-rutile phase transformation. The results of photodegrading methyl orange showed holmium doping improved the photocatalytic activity of TiO₂, and the reasons could be attributed to the synergetic effects of large surface areas, small crystallite size, lattice distortion and more charge imbalance of holmium-doped TiO₂. In our experiment, the optimal doped amount was 0.3 mol.% for the maximum photocatalytic degradation ratio when holmium-doped TiO₂ was calcined at 500 °C, and the optimal calcined temperature was 600 °C when the doped amount was 0.5 mol.%.