Phase evolution and thermophysical properties of high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ oxides

Pursuing novel thermal barrier–coating materials with lower thermal conductivity and high-temperature stability can simultaneously improve the working efficiency and service temperature of a gas turbine. In this study, a series of high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ (RE = La, Nd, Sm, Gd, Dy, and Er) oxides were prepared though solid-state reaction. Through tuning the rare-earth cations, an order–disorder transition occurs from certain partially ordered weberite structure (C222₁) to disordered defective fluorite structure (Fm (Formula presented.) m). All the high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ oxides possess low thermal conductivity in the range of 0.91–1.34 W m⁻¹ K⁻¹ at room temperature, which can be attributed to increased lattice anharmonicity and disorder, resulting in additional phonon scattering. Herein, we proved that the incorporation of heterovalent cations at B-sites in high-entropy A₂B₂O₇ crystals is an effective strategy to reduce the thermal conductivity without compromising the decrease of oxygen vacancy. Moreover, the high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ oxides show the relatively higher thermal expansion coefficients of 10.3–10.7 × 10⁻⁶°C⁻¹ and excellent phase stability at elevated temperatures.