Nanobubble fragmentation and bubble-free-channel shear localization in helium-irradiated submicron-sized copper

Helium bubbles are one of the typical radiation microstructures in metals and alloys, significantly influencing their deformation behavior. However, the dynamic evolution of helium bubbles under straining is less explored so far. Here, by using in situ micromechanical testing inside a transmission electron microscope, we discover that the helium bubble not only can coalesce with adjacent bubbles, but also can split into several nanoscale bubbles under tension. Alignment of the splittings along a slip line can create a bubble-free channel, which appears softer, promotes shear localization, and accelerates the failure in the shearing-off mode. Detailed analyses unveil that the unexpected bubble fragmentation is mediated by the combination of dislocation cutting and internal surface diffusion, which is an alternative microdamage mechanism of helium irradiated copper besides the bubble coalescence.