TY - JOUR
T1 - Microwave dielectric properties of (ABi)1/2MoO4 (A = Li, Na, K, Rb, Ag) type ceramics with ultra-low firing temperatures
AU - Zhou, Di
AU - Randall, Clive A.
AU - Pang, Li Xia
AU - Wang, Hong
AU - Guo, Jing
AU - Zhang, Gao Qun
AU - Wu, Ying
AU - Guo, Ke Ting
AU - Shui, Li
AU - Yao, Xi
PY - 2011/10/3
Y1 - 2011/10/3
N2 - A series of (ABi)1/2MoO4 (A = Li, Na, K, Rb, Ag) compositions were studied in regard to the sintering behavior, phase composition, microwave dielectric properties and chemical compatibility with silver and/or aluminum for electrodes. All the (ABi)1/2MoO 4 (A = Li, Na, K, Rb, Ag) ceramics could be sintered below 700 °C with relative densities above 93%. Whereas the (KBi)1/2MoO 4 ceramic can be sintered to a high density at around 630 °C/2 hrs with a relative permittivity ∼37, a Qf value of 4000 GHz and a temperature coefficient of resonant frequency (TCF) ∼ +117 ppm/°C. Furthermore, from the XRD analysis of co-fired ceramics, the (KBi) 1/2MoO4 ceramic reacts with silver but not with aluminum at its densification temperature. The (ABi)1/2MoO4 (A = Li, Na, K, Rb, Ag) type ceramics can all be considered into the new field of ultra-low temperature co-firing dielectrics for multilayer applications.
AB - A series of (ABi)1/2MoO4 (A = Li, Na, K, Rb, Ag) compositions were studied in regard to the sintering behavior, phase composition, microwave dielectric properties and chemical compatibility with silver and/or aluminum for electrodes. All the (ABi)1/2MoO 4 (A = Li, Na, K, Rb, Ag) ceramics could be sintered below 700 °C with relative densities above 93%. Whereas the (KBi)1/2MoO 4 ceramic can be sintered to a high density at around 630 °C/2 hrs with a relative permittivity ∼37, a Qf value of 4000 GHz and a temperature coefficient of resonant frequency (TCF) ∼ +117 ppm/°C. Furthermore, from the XRD analysis of co-fired ceramics, the (KBi) 1/2MoO4 ceramic reacts with silver but not with aluminum at its densification temperature. The (ABi)1/2MoO4 (A = Li, Na, K, Rb, Ag) type ceramics can all be considered into the new field of ultra-low temperature co-firing dielectrics for multilayer applications.
KW - Ceramics
KW - Dielectric properties
KW - Electronic materials
KW - LTCC
KW - Microwave dielectric
UR - https://www.scopus.com/pages/publications/79960556831
U2 - 10.1016/j.matchemphys.2011.05.040
DO - 10.1016/j.matchemphys.2011.05.040
M3 - 文章
AN - SCOPUS:79960556831
SN - 0254-0584
VL - 129
SP - 688
EP - 692
JO - Materials Chemistry and Physics
JF - Materials Chemistry and Physics
IS - 3
ER -