Microwave dielectric properties and co-firing with copper of (Bi_1-xCu_x)(Nb_1-xW_x)O₄ ceramics

Effect of substitution of CuO and WO₃ on the microwave dielectric properties of BiNbO₄ ceramics and the co-firing between ceramics and copper electrode were investigated. The (Bi_1-xCu_x)(Nb_1-xW_x)O₄ (x = 0.005, 0.01, 0.015, 0.02) composition can be densified between 900 and 990 °C. The microwave dielectric constants lie between 36 and 45 and the pores in ceramics were found to be the main influence. The Q values changes between 1400 and 2900 with different x values and sintering temperatures while Q_f values lie between 6000 and 16,000 GHz. The microwave dielectric losses, mainly affected by the grain size, pores, and the secondary phase, are discussed. The (Bi_1-xCu_x)(Nb_1-xW_x)O₄ ceramics and copper electrode was co-fired under N₂ atmosphere at 850 °C and the EDS analysis showed no reaction between the dielectrics and copper electrodes. This result presented the (Bi_1-xCu_x)(Nb_1-xW_x)O₄ dielectric materials to be good candidates for LTCC applications with copper electrode.