Microstructure and properties of porous Ni50Cr50-Al₂O ₃ cermet support for solid oxide fuel cells

Microstructure of cermet support influences significantly the performance and stability of solid oxide fuel cells (SOFCs). The properties required for the support include high electrical conductivity, necessary permeability, good match of thermal expansion with other layers and high temperature strength. In this study, a porous Ni50Cr50-Al₂O₃ cermet was designed as the support of SOFC. The porous cermet was deposited by flame spraying with a powder mixture of 30%vol Al₂O₃ and 35%vol Ni50Cr50 and 35%vol polyester. The effect of cermet microstructure on its gas permeability was investigated. The electrical conductivity, thermal expansion coefficient and bending strength of cermet support were also studied. The results showed that the gas leakage rate of the cermet support increased with the increase of polyester content in the starting powder. The thermal expansion coefficient of the composite cermet decreased with the increase of the volume fraction of Al₂O₃. Moreover, the electric conductivity of the cermet increased significantly after high temperature sintering, and reached 1015 S/cm after sintering at 1000°C for 15 hours. The three point bending strength of the Ni50Cr50-based cermet support reached 171 MPa. The cermet stability at high temperatures and SOFCs performance were discussed.