T1 - Crystal structure, impedance and broadband dielectric spectra of ordered scheelite-structured Bi(Sc1/3Mo2/3)O4 ceramic
AU - Zhou, Di
AU - Pang, Li Xia
AU - Wang, Da Wei
AU - Guo, Huan Huan
AU - Yang, Fan
AU - Qi, Ze Ming
AU - Li, Chun
AU - Jin, Biao Bing
AU - Reaney, Ian M.
N1 - Publisher Copyright:
© 2017 Elsevier Ltd
PY - 2018/4
Y1 - 2018/4
N2 - Bi(Sc1/3Mo2/3)O4 ceramics were prepared via solid state reaction method. It crystallized with an ordered scheelite-related structure (a = 16.9821(9) Å, b = 11.6097(3) Å, c = 5.3099(3) Å and β = 104.649(2)°) with a space group C12/C1, in which Bi3+, Sc3+ and Mo6+ are −8, −6 and −4 coordinated, respectively. Bi(Sc1/3Mo2/3)O4 ceramics were densifiedat 915 °C, giving a permittivity (εr) ∼24.4, quality factor (Qf, Q = 1/dielectric loss, f = resonant frequency) ∼48, 100 GHz and temperature coefficient of resonant frequency (TCF) ∼ −68 ppm/°C. Impedance spectroscopy revealed that there was only a bulk response for conductivity with activation energy (Ea) ∼0.97 eV, suggesting the compound is electrically and chemically homogeneous. Wide band dielectric spectra were employed to study the dielectric response of Bi(Sc1/3Mo2/3)O4 from 20 Hz to 30 THz. εr was stable from 20 Hz to the GHz region, in which only ionic and electron displacive polarization contributed to the εr.
AB - Bi(Sc1/3Mo2/3)O4 ceramics were prepared via solid state reaction method. It crystallized with an ordered scheelite-related structure (a = 16.9821(9) Å, b = 11.6097(3) Å, c = 5.3099(3) Å and β = 104.649(2)°) with a space group C12/C1, in which Bi3+, Sc3+ and Mo6+ are −8, −6 and −4 coordinated, respectively. Bi(Sc1/3Mo2/3)O4 ceramics were densifiedat 915 °C, giving a permittivity (εr) ∼24.4, quality factor (Qf, Q = 1/dielectric loss, f = resonant frequency) ∼48, 100 GHz and temperature coefficient of resonant frequency (TCF) ∼ −68 ppm/°C. Impedance spectroscopy revealed that there was only a bulk response for conductivity with activation energy (Ea) ∼0.97 eV, suggesting the compound is electrically and chemically homogeneous. Wide band dielectric spectra were employed to study the dielectric response of Bi(Sc1/3Mo2/3)O4 from 20 Hz to 30 THz. εr was stable from 20 Hz to the GHz region, in which only ionic and electron displacive polarization contributed to the εr.
KW - Bi(ScMo)O
KW - Low temperature co-fired ceramic (LTCC)
KW - Microwave dielectric
UR - https://www.scopus.com/pages/publications/85039748351
U2 - 10.1016/j.jeurceramsoc.2017.12.044
DO - 10.1016/j.jeurceramsoc.2017.12.044
M3 - 文章
AN - SCOPUS:85039748351
SN - 0955-2219
VL - 38
SP - 1556
EP - 1561
JO - Journal of the European Ceramic Society
JF - Journal of the European Ceramic Society
IS - 4
ER -